项目 |
典型值 |
测试标准 |
|
固化前性能 ( 23±2℃/50±5%RH ) |
||
|
外观 |
灰色膏状物 |
目测 |
|
比重(g/cm3) |
3.2±0.5 |
GB/T 533-2008 |
|
固化后性能 ( 23±2℃/50±5%RH×7days ) |
||
|
固化条件120℃(Min) |
30 |
-- |
|
邵氏硬度(Shore A) |
80±10 |
GB/T 531.1—2008 |
|
断裂伸长率(%) |
≥45 |
GB/T 528—2009 |
|
拉伸强度(MPa) |
≥4.5 |
GB/T 528—2009 |
|
导热率(W/(m.K)) |
3.0±0.2 |
ISO22007-2 |
|
剪切强度 AI/AI(MPa) |
≥4.5 |
GB/T 7124—2008 |
|
介电强度(kV/mm) |
22 |
GB/T 1408.1—2006 |
|
介电常数（1MHz） |
≤4.0 |
GB/T 1409—2006 |
|
体积电阻率(Ω·cm) |
≥1.0×1013 |
GB/T 1410—2006 |
|
工作温度(℃) |
-50～200 |
|
|
基材 |
效果 |
粘结强度 |
|
金属 |
||
|
铝 |
极佳 |
1.5 |
|
黄铜 |
极佳 |
1.8 |
|
铜 |
极佳 |
1.7 |
|
软钢 |
极佳 |
1.7 |
|
不锈钢 |
极佳 |
1.8 |
|
塑料及树脂 |
||
|
树脂 |
极佳 |
1.9 |
|
丙烯酸树脂 |
差 |
0.8 |
|
环氧树脂 |
极佳 |
1.7 |
|
酚醛树脂 |
极佳 |
1.5 |
|
聚缩醛 （POM） |
极佳 |
1.6 |
|
聚对苯二甲酸丁二醇脂（PBT） |
极佳 |
1.5 |
|
聚碳酸脂（PC） |
好 |
1.3 |
|
聚酯薄膜（PET） |
极佳 |
1.5 |
|
聚乙烯（PE） |
application
The product is suitable for various electronic and electrical applications, as well as applications that require bonding, sealing, thermal conductivity, insulation, protection, moisture-proof, dustproof, etc.
Usage methodInstructions for use
● Clean and dry the surface of the adhesive object, and remove any pollutants such as rust, dust, and oil that may affect adhesion.
● Extrude the adhesive with a special tool and apply it to the cleaned joint surface.
● After the adhesive application is completed, it is moved into an oven or heated environment for curing. According to the actual situation, it is better to extend the curing time and increase the curing temperature appropriately.
matters needing attention
● Rubber materials should be stored in a sealed low temperature (below 25 ℃), and long-term storage at room temperature or high temperature environment will shorten the storage period.
● This product is not a hazardous material, but avoid contact with skin and eyes.
● Contact with a certain amount of the following chemical substances can cause the adhesive to not cure or cure incompletely:
1.Organic compounds containing N, P, and S.
2.Ionic compounds containing elements such as Sn, Pb, Hg, and As.
3.Compounds containing alkynes and polyvinyls.
● In order to avoid the above phenomenon, before using glue sealing, the residual rosin on the device should be wiped clean as much as possible, and solder with low lead content should be used as much as possible.
● After use, the rubber hose of this product should be sealed for storage and reuse. This product is for industrial use only.
Packaging specifications
● 300ml/bottle, 24 bottles per box.
Storage and transportation
● Store away from children.
● This product has a storage period of six months in an environment below 25 ℃.
● This product is non hazardous and is stored and transported as a general chemical.